Summary of product information
- Appearance: Clear liquid
- Polymer type: With Polyisocyanates Cross-Linkable
- Category: Xylene/MPA(1:1)
- Category: Two Component Hydroxy Acrylic Resins
Product Information
A hydroxyl functional acrylic resin designed for crosslinking with polyisocyanates, specially used in repairing automotive paints and clear coats.
Product Supplementation
Appearance | Clear liquid |
Type | With Polyisocyanates Cross-Linkable |
Solvent | Xylene/MPA(1:1) |
Solubility | Soluble in:
Partially soluble in:
|
Color
|
<70 |
Solids(%)(ASTM D-1259) | 60±1 |
Acid value(mg KOH/g)(ASTM D-1639) | 5-10 |
Hydroxyl content(%)(ASTM D-4274) | 4.5 |
Viscosity at 25°C (cP)(ASTM D-562) | 2500-5000 |
Density at 25°C(g/ml)(ASTM D-1475) | 1.03 |
Flash point(°C)(ASTM D-93) | 24 |
• Superior outdoor stability
• Very good chemical resistance
• Excellent gloss
• In combination with aliphatic polyisocyanates at ambient temperature drying or forced drying.
• Coatings reach to their optimum properties after 10 to 12 days, but it forced dried 30 minutes at 80°C is sufficient for curing.
• See our guide formulation for specific information.
• Should be avoided using alcohol and glycol solvents.
• The principal application is in producing automotive refinishes as top coats and clear coats.
• Should be kept in sealed containers at temperature not exceeding 35°C and well ventilated area for a maximum 12 month.